| Customization: | Available |
|---|---|
| CAS No.: | 9009-54-5 |
| EINECS: | 31692-79-2 |
|
Still deciding? Get samples of US$ 0/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product | Universal Acidic Acetic Silicone Adhesive & Sealant |
| Model No. | Jinguiyuan 517 |
| Type | Acetic Curing, RTV curing |
| Color | Clear, Black, White, Gray or as customized |
| Usage temperature | +5ºC~+40ºC |
| Applicated temperature | -40ºC~+150°ºC |
| Packing | 260ml/280ml/300ml/310ml/Cartridge, 24pcs/Carton; 200L Barrel |
| Shelf life | 12 months |
Features:
1. Never turn white;
2. Fast curing speed, durable seal;
3. Good adhesion and compatibility to most building materials;
4. Excellent weather ability and high resistance to UV radiation, heat, humidity, ozone, and high temperature;
Main Applications:
- Installation of various doors and windows;
- Bonding and sealing of various glassworks;
- Indoor decoration joint sealing;
- Handicraft bonding;
- General bonding and sealing of various signs, glass display cabinets, etc.
Use Limitations
1. All the surfaces that bleed oils, plasticizers, or solvents;
2. Non-corrosion-resistant substrates such as concrete, porous stones (like marble), coated glass, copper, lead, and galvanized materials;
3. The mucilage shall not be completely isolated from the air before fully curing;
4. The frosty or moist surface;
5. When the surface's temperature is below 4ºC or above 40ºC.
| Acetic General Silicone Sealant | ||||
| Performance | Standard | Measured Value | Testing Method | |
| Test at 50±5% RH and temperature 23±2ºC | ||||
| Density (g/cm³) | ±0.1 | 0.95 | GB/T 13477 | |
| Tack-free Time (min) | ≤180 | 10 | GB/T 13477 | |
| Extrusion g/5S | ≥40 | 102 | GB/T 13477 | |
| Tensile Modulus (Mpa) | 23ºC | ≤0.4 | 0.28 | GB/T 13477 |
| -20ºC | or ≤0.6 | 0.3 | ||
| 105ºC weight loss, 24hr % | / | 55 | GB/T 13477 | |
| Slumpability (mm) Vertical | ≤3 | 0 | GB/T 13477 | |
| Slumpability (mm) Horizontal | 0 | 0 | GB/T 13477 | |
| Curing Speed (mm/d) | 2 | 2.5 | / | |
| As Cured-after 21 days at 50±5% RH and Temperature 23±2ºC | ||||
| Hardness (Shore A) | 20-60 | 22 | GB/T 531 | |
| Tensile Strength under Standard Conditions (Mpa) | / | 0.12 | GB/T 13477 | |
| Elongation of Rupture (%) | / | 500 | GB/T 13477 | |
| Movement Capability (%) | 12.5 | 12.5 | GB/T 13477 | |